PA66 A 216 V30法国罗地亚TECHNYL 30%玻纤增强尼龙66塑料（18024445500）

TECHNYL A 216 V30 　 　 Product Data Sheet 21.11.2014
　 　 　 Properties 　
　 Typical values of properties are for natural grades
　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ISO 62 % 0,80 　
Density ISO 1183/A g/cm3 1,37 　
Molding shrinkage Parallel RHODIA % 0,50 　
Molding shrinkage normal or perpendicular RHODIA % 0,80 　
Molding Shrinkage Isotropy RHODIA 　 0,62 　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 10000　7500　
Tensile strength at break ISO 527 Type 1A MPa 190　135　
Elongation at break ISO 527 Type 1A % 3　　
Flexural modulus ISO 178 MPa 8400　5900　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 12　16　
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 80　95　
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 11　16　
Flammability 　 　 　 　
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 　 HB 　
Glow Wire Flammability Index (Thickness: 3,2 mm) ISO 60695-2-12 °C 750　　
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 650　　
Glow Wire Ignition Temperature (Thickness: 1,6 ISO 60695-2-13 °C 650　　
mm) 　 　 　 　
Limit Oxygen Index ISO 4589 　 23　　
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　　
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 255　　
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 2,5 　
85°C) 　 　 　 　
Electrical 　 　 　 　
Comparative tracking index (Sol A) IEC 60112 V 600　600　
Comparative tracking index (Sol B) IEC 60112 V 500　500　
Dielectric strength IEC 60243 kV/mm 40　30　
Dissipation factor IEC 60250 　 0,010 0,110
Relative permittivity IEC 60250 　 3,75 4　
Surface resistivity IEC 60093 Ohm 6E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 1E 15 2E 13