PA66 A 218 V30 BLACK 21 NS法国罗地亚TECHNYL热稳定尼龙66塑料（18024445500）









TECHNYL A 218 V30 BLACK 21 NS 　 　 　 　
　 　 　 Properties 　
　 Typical values of properties are for natural grades
　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ISO 62 % 0,80 　
　 ASTM D-792 % 0,80 　
Density ISO 1183/A g/cm3 1,37 　
Molding shrinkage Parallel RHODIA % 0,50 　
Molding shrinkage normal or perpendicular RHODIA % 0,80 　
Molding Shrinkage Isotropy RHODIA 　 0,62 　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 10000　7500　
Tensile strength at break ISO 527 Type 1A MPa 190　135　
Elongation at break ISO 527 Type 1A % 3　6　
Flexural modulus ISO 178 MPa 9000　6400　
　 ASTM D-790 MPa 9000　　
Flexural maximum stress ISO 178 MPa 280　185　
　 ASTM D-790 MPa 290　　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 11　15　
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 80　88　
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 10　18　
　 ASTM D256 J/m 115　　
Izod unnotched impact strength ISO 180/1U kJ/m2 60　65　
Flammability 　 　 　 　
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 　 HB 　
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 700　　
Limit Oxygen Index ISO 4589 　 23　　
Fire and Smoke index NF F 16 101 　 I2 / F3 　
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　　
　 ASTM D3417 °C 260　　
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 255　　
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 255　　
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 2,5 　
perpendicular (23°C to 85°C) 　 　 　 　
Coef of Linear thermal expansion parallel (23°C to ISO 11359 E-5/°C 2,5 　
85°C) 　 　 　 　
Electrical 　 　 　 　
Comparative tracking index (Sol A) IEC 60112 V 600　600　
Comparative tracking index (Sol B) IEC 60112 V 500　　
Dielectric strength IEC 60243 kV/mm 34　29　
Dissipation factor IEC 60250 　 0,010 0,110
Relative permittivity IEC 60250 　 3,70 4　
Surface resistivity IEC 60093 Ohm 6E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 1E 15 1E 13