PA66 A 218 V35 BLACK 21 N法国罗地亚TECHNYL 35%玻纤增强热稳定尼龙66塑料（18024445500）









TECHNYL A 218 V35 BLACK 21 N 　 　 　 　
　 　 　 Properties
　 Typical values of properties are for natural grades
　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ISO 62 % 0,75 　
　 ASTM D-792 % 0,75 　
Density ASTM D-792 g/cm3 1,41 　
Molding shrinkage Parallel RHODIA % 0,45 　
Molding shrinkage normal or perpendicular RHODIA % 0,75 　
Molding Shrinkage Isotropy RHODIA 　 0,60 　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 11400　8700　
Tensile strength at break ISO 527 Type 1A MPa 210　150　
Elongation at break ISO 527 Type 1A % 3　5　
Flexural modulus ISO 178 MPa 9500　6800　
　 ASTM D-790 MPa 9800　　
Flexural maximum stress ASTM D-790 MPa 290　　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 13,5 18,5
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 95　100　
Izod notched impact strength (23 °C) ISO 180/1A kJ/m2 13　18　
　 ASTM D256 J/m 120　　
Flammability 　 　 　 　
Flammability (Thickness: 0,8 mm) ISO 1210 / UL94 　 HB 　
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 　 HB 　
Flammability (Thickness: 3,2 mm) ISO 1210 / UL94 　 HB 　
Limit Oxygen Index ISO 4589 　 23　　
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　　
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 255　　
　 ASTM D-648 °C 255　　
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 2,2 　
perpendicular (23°C to 85°C) 　 　 　 　
Electrical 　 　 　 　
Comparative tracking index (Sol A) IEC 60112 V 600　600　
Dielectric strength IEC 60243 kV/mm 34　29　
Dissipation factor IEC 60250 　 0,010 0,110
Relative permittivity IEC 60250 　 3,70 4　
Surface resistivity IEC 60093 Ohm 6E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 1E 15 1E 13