PA66 A 218G V33 BLACK 34N法国罗地亚TECHNYL 33%玻纤增强热稳定尼龙66塑料（18024445500）









TECHNYL A 218G V33 BLACK 34N 　 　 　 　
　 　 　 Properties
　 Typical values of properties are for black grades
　 Standards Unit Values 　
　 　 　 d.a.m. Cond.
Physical 　 　 　 　
Water absorption(24h at 23°C) ASTM D-792 % 0,80 　
Density ISO 1183/A g/cm3 1,39 　
Molding shrinkage Parallel RHODIA % 0,40 　
Molding shrinkage normal or perpendicular RHODIA % 1　　
Mechanical 　 　 　 　
Tensile Modulus ISO 527 Type 1A MPa 11500　7900　
Tensile strength at break ISO 527 Type 1A MPa 200　140　
　 ASTM D-638 MPa 195　　
Elongation at break ISO 527 Type 1A % 3,40 　
　 ASTM D-638 % 3　　
Flexural modulus ISO 178 MPa 9500　7000　
　 ASTM D-790 MPa 9500　　
Flexural maximum stress ASTM D-790 MPa 295　　
Charpy notched impact strength (23 °C) ISO 179/1eA kJ/m2 12　19　
Charpy unnotched impact strength (23 °C) ISO 179/1eU kJ/m2 92　98　
Izod notched impact strength (23 °C) ASTM D256 J/m 120　　
　 ISO 180/1A kJ/m2 13　20　
Flammability 　 　 　 　
Flammability (Thickness: 1,6 mm) ISO 1210 / UL94 　 HB 　
Glow Wire Flammability Index (Thickness: 1,6 mm) ISO 60695-2-12 °C 700　　
Limit Oxygen Index ISO 4589 　 23　　
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 260　　
Heat deflection temperature (1,8 MPa) ISO 75/Af °C 250　　
Heat deflection temperature (1,82 MPa) ASTM D-648 °C 255　　
Coef of Linear thermal expansion normal or ISO 11359 E-5/°C 2,5 　
perpendicular (23°C to 85°C) 　 　 　 　
Electrical 　 　 　 　
Comparative tracking index (Sol A) IEC 60112 V 450　425　
Dielectric strength IEC 60243 kV/mm 34　29　
Dissipation factor IEC 60250 　 0,010 0,110
Relative permittivity IEC 60250 　 3,70 4　
Surface resistivity IEC 60093 Ohm 6E 14 1E 12
Volume resistivity IEC 60093 Ohm/cm 5E 14 1E 13