PA66 A 218W V30 BLACK FA法国罗地亚TECHNYL® 30%玻纤增强热稳定耐水解尼龙66塑料（18024445500）

TECHNYL® A 218W V30 BLACK FA
The values of properties are for black grade.
Properties Standards Unit Values 　
　 　 　 d.a.m*. Cond.**
Physical 　 　 　 　
Water absorption (24 h at 23°C) ISO 62 % 0.80　-
Density ISO 1183-A g/cm3 1.35　-
Molding shrinkage Parallel (1) (RHODIA-EP) RHODIA-EP % 0.5　-
Molding shrinkage normal or perpendicular (1) (Rhodia EP) RHODIA-EP % 0.80　-
Molding Shrinkage Isotropy (Rhodia EP) RHODIA-EP 　 0.62　-
Mechanical 　 　 　 　
Tensile modulus ISO 527 type 1 A MPa 10000　7500　
Elongation at break ISO 527 type 1 A % 3　4　
Tensile strength at break ISO 527 type 1 A MPa 185　130　
Flexural modulus ISO 178 MPa 9000　6400　
Flexural maximum stress ISO 178 MPa 275　180　
Charpy notched impact strength ISO 179/1eA kJ/m2 11　15　
Charpy unnotched impact strength ISO 179/1eU kJ/m2 80　90　
Izod notched impact strength ISO 180/1A kJ/m2 10　17　
Flamability 　 　 　 　
Flammability UL 94 (Thickness 0,8 mm) ISO 1210/UL 94 　 HB -
Flammability UL 94 (Thickness 1,6 mm) ISO 1210/UL 94 　 HB -
Flammability UL 94 (Thickness 3,2 mm) ISO 1210/UL 94 　 HB -
Glow wire flammability index (thickness = 1,6) IEC60695-2-12 °C 700　-
Thermal 　 　 　 　
Melting Temperature ISO 11357 °C 263　-
Heat deflection temperature, 1,8 Mpa ISO 75/Af °C 255　-
Coef. of Linear thermal expansion parallel (23°C to 85°C) ISO 11359 E-5 / °C 2.80　-
Electrical 　 　 　 　
Relative permittivity IEC60250 　 3.70　3.30　
Dissipation factor IEC60250 　 0.02　0.08　
Volume resistivity IEC60093 Ohm.cm 10E14 10E11
Surface resistivity IEC60093 Ohm 10E13 10E11
Dielectric strength IEC60243 kV/mm 35　-
Comparative tracking index sol. A IEC60112 Volt 600　-