PA6 B 30 S FN30 000000德国朗盛Durethan无卤阻燃耐热老化稳定尼龙6塑料(18024445500)
PA 6, non-reinforced, injection molding, halogen free flame retardant, heat-aging resistance
ISO Shortname: ISO 1874-PA 6, GFHR, 12-030; ISO 1043-PA FR (30)
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.9
C Molding shrinkage, transverse 60x60x2; 260 °C / MT 80 °C; 600 bar % ISO 294-4 0.9
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.3
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.3
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 3700 1200
C Yield stress 50 mm/min MPa ISO 527-1,-2 80 40
C Yield strain 50 mm/min % ISO 527-1,-2 3.5 20
C Nominal strain at break 50 mm/min % ISO 527-1,-2 10 >50
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 80 50
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 14 >50
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 75 75
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10 15
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 90 N |