PA6 B 31 FCS 000000德国朗盛Durethan挤出低粘度聚酰胺6尼龙塑料(18024445500)
PA 6, non-reinforced, extrusion, low viscosity, slip agent
ISO Shortname: ISO 1874 PA 6, ES, 14-030
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Melt volume-flow rate 235 °C; 2.16 kg cm³/(10 min) ISO 1133-1 16
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 2800 800
C Yield stress 50 mm/min MPa ISO 527-1,-2 75 35
C Yield strain 50 mm/min % ISO 527-1,-2 4 25
C Nominal strain at break 50 mm/min % ISO 527-1,-2 20 >50
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU N N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU N 55
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 5 50
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA 5 <5
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U N N
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U N N
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A 7 50
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A 7 7,5
Flexural modulus 2 mm/min MPa ISO 178-A 2600 700
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5 8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 90 20
Ball indentation hardness N/mm&sup2; ISO 2039-1 140 50 |