PA6 BKV 130 H2.0 DUS008 901510德国朗盛Durethan 30%玻纤增强耐冲击耐热老化尼龙6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6-HI, GHR, 14-090, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.3　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.8　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9300 5200
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 160 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.4 8.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 75 75
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 13 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m² ISO 180-1U 80 85
Izod impact strength -30 °C kJ/m² ISO 180-1U 70 70
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15 22
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 8600 4700
Flexural strength 2 mm/min MPa ISO 178-A 250 155
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.3 6.7
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 240 125
C Puncture maximum force 23 °C N ISO 6603-2 990　
C Puncture maximum force -30 °C N ISO 6603-2 765　
C Puncture energy 23 °C J ISO 6603-2 4.3　
C Puncture energy -30 °C J ISO 6603-2 2.5