PA6 BKV 30 H2.0 000000德国朗盛Durethan 30%玻纤增强热老化稳定尼龙6塑料（18024445500）
PA 6, 30 % glass fibers, injection molding, heat-aging stabilized
ISO/ ASTM
ISO Shortname: ISO 1874-PA 6, MHR, 14-100, GF30
Property Test Condition Unit Standard guide value
d.a.m. cond.
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9600 5900
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 170 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.5 6.5
C Tensile creep modulus 1000 h MPa ISO 899-1 4100
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 80 95
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 70 70
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 15 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 10 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 75 80
Izod impact strength -30 °C kJ/m² ISO 180-1U 65 65
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15 20
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 8500 5100
Flexural strength 2 mm/min MPa ISO 178-A 280 170
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 265 140
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 ~200
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 ~215
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 ~110
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 > 200 |