PA6 BKV 30 H2.0 901510德国朗盛Durethan 30%玻纤增强热老化稳定尼龙6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, heat-aging stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 6, GHR, 14-090, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.3　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.69　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.06　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.13　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9500 5800
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 170 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 6.0
C Tensile creep modulus 1 h MPa ISO 899-1　5100
C Tensile creep modulus 1000 h MPa ISO 899-1　4100
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 75 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 65 60
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10 20
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 65 80
Izod impact strength -30 °C kJ/m² ISO 180-1U 60 55
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10 20
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 8500 5000
Flexural strength 2 mm/min MPa ISO 178-A 270 160
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.0 6.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 260 140
C Puncture maximum force 23 °C N ISO 6603-2 1000 1230
C Puncture maximum force -30 °C N ISO 6603-2 860　
C Puncture energy 23 °C J ISO 6603-2 3 6
C Puncture energy -30 °C J ISO 6603-2 3　
Ball indentation hardness　N/mm² ISO 2039-1 210 100