PA6 BKV 50 H2.0 EF DUS030 901510德国朗盛Durethan 50%玻纤增强流动性改进尼龙6塑料（18024445500）

PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized



ISO Shortname: ISO1874-PA 6, GHR, 10-160, GF50

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.20　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.60　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.10　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16000 9000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 215 130
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5 4
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 90　
Izod impact strength 23 °C kJ/m² ISO 180-1U 80 80
Izod impact strength -30 °C kJ/m² ISO 180-1U 80　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 15　
Flexural modulus 2 mm/min MPa ISO 178-A 15000 9500
Flexural strength 2 mm/min MPa ISO 178-A 320 205
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0 4.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　200
C Puncture maximum force 23 °C N ISO 6603-2 1000　
C Puncture maximum force -30 °C N ISO 6603-2 900　
C Puncture energy 23 °C J ISO 6603-2 3.7　
C Puncture energy -30 °C J ISO 6603-2 3.5　

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 220　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 213　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 220　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.1　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.8　

Other properties (23 °C)
C Density　kg/m³ ISO 1183 1570　
Bulk density　kg/m³ ISO 60 700　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.12　
Melt temperature (Tmin - Tmax)　°C - 270-290　
Mold temperature　°C - 80-120　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.