PA6 BKV 50 H3.0 000000德国朗盛Durethan 50%玻纤增强热老化稳定尼龙6塑料（18024445500）

PA 6, 50 % glass fibers, injection molding, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6, GHR, 14-160, GF50

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.16　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 400 bar % acc. ISO 2577 0.85　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.02　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.05　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16800 10200
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 225 140
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 5.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 100 110
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 90 90
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 20 25
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 15 15
Izod impact strength 23 °C kJ/m² ISO 180-1U 95 100
Izod impact strength -30 °C kJ/m² ISO 180-1U 95 95
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 20 25
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 15 15
Flexural modulus 2 mm/min MPa ISO 178-A 15500 9900
Flexural strength 2 mm/min MPa ISO 178-A 360 230
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0 5.0

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 205　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 215　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 > 200　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.2　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.7　
C Burning behavior UL 94 (1.6 mm) 1.6 mm Class UL 94 HB　
Burning behavior UL 94 3.2 mm Class UL 94 HB　
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650　
Burning behavior US-FMVSS302 >=1.0 mm　ISO 3795 passed　
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 > 200　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 5.0　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 1.5　
C Density　kg/m³ ISO 1183 1570　
Bulk density　kg/m³ ISO 60 700　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.03-0.12　
Melt temperature (Tmin - Tmax)　°C - 270-290　
Mold temperature　°C - 80-120　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.