PA6 BKV 60 H2.0 EF DUS060 900116德国朗盛Durethan 60%玻纤增强热老化稳定尼龙6塑料（18024445500）

PA 6, 60 % glass fibers, injection molding, improved flowability, heat-aging stabilized



ISO Shortname: ISO1874-PA 6, GHR, 10-220, GF60

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.32　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.40　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.03　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.06　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 20000 12000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 225 145
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.4 3.5
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 90 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 90 90
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 16　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 16　
Izod impact strength 23 °C kJ/m² ISO 180-1U 80 80
Izod impact strength -30 °C kJ/m² ISO 180-1U 80 80
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 16 20
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 16　
Flexural modulus 2 mm/min MPa ISO 178-A 19300 12800
Flexural strength 2 mm/min MPa ISO 178-A 365 235
Flexural strain at flexural strength 2 mm/min % ISO 178-A 2.8 3.6
Ball indentation hardness　N/mm² ISO 2039-1 255 155

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 222　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 213　
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 220　
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 210　
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.12　
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 0.75　

Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 5.3 11.2
C Relative permittivity 1 MHz - IEC 60250 4.7 5.1
C Dissipation factor 100 Hz 10-4 IEC 60250 164 2149
C Dissipation factor 1 MHz 10-4 IEC 60250 177 651
C Volume resistivity　Ohm·m IEC 60093 5.8E12 8E9
C Electric strength 1 mm kV/mm IEC 60243-1 33 33
C Comparative tracking index CTI Solution A V IEC 60112 600　

Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 3.6　
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 1.3　
C Density　kg/m³ ISO 1183 1700　
Bulk density　kg/m³ ISO 60 750　

Processing conditions for test specimens
C Injection molding-Melt temperature　°C ISO 294 280　
C Injection molding-Mold temperature　°C ISO 294 80　

Processing recommendations
Drying temperature dry air dryer　°C - 80　
Drying time dry air dryer　h - 2-6　
Residual moisture content　% Acc. to Karl Fischer　0.06-0.20　
Melt temperature (Tmin - Tmax)　°C - 270-290　
Mold temperature　°C - 80-120　

C These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.