PA6 BKV 215 000000德国朗盛Durethan 15%玻纤增强耐冲击尼龙6塑料（18024445500）
PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength
ISO Shortname: ISO 1874-PA 6/66HI, GR, 14-040, GF15
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.59
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.61
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.14
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.15
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 4500 2400
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 85 55
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 4.5 15
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 70 80
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 80 75
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 20 35
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 12 12
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 18 30
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 10 10
Flexural modulus 2 mm/min MPa ISO 178-A 4000 2200
Flexural strength 2 mm/min MPa ISO 178-A 130 80
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.0 7.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 125 60
C Puncture maximum force 23 °C N ISO 6603-2 1003
C Puncture maximum force -30 °C N ISO 6603-2 650
C Puncture energy 23 °C J ISO 6603-2 13 32
C Puncture energy -30 °C J ISO 6603-2 4.8
Ball indentation hardness N/mm² ISO 2039-1 110 55
Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 214
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 175
C Temperature of deflection under load 0.45 MPa °C ISO 75-1,-2 205
C Temperature of deflection under load 8.00 MPa °C ISO 75-1,-2 60
Vicat softening temperature 50 N; 120 °C/h °C ISO 306 200
C Coefficient of linear thermal expansion, parallel 23 to 55 °C 10-4/K ISO 11359-1,-2 0.4
C Coefficient of linear thermal expansion, transverse 23 to 55 °C 10-4/K ISO 11359-1,-2 1.5
C Burning behavior UL 94 (1.6 mm) 1.6 mm Class UL 94 HB
Burning behavior UL 94 3.2 mm Class UL 94 HB
C Oxygen index Method A % ISO 4589-2 22
Glow wire test (GWFI) 2.0 mm °C IEC 60695-2-12 650
Burning behavior US-FMVSS302 ISO 3795 passed
C Vicat softening temperature 50 N; 50 °C/h °C ISO 306 200
Electrical properties (23 °C/50 % r. h.)
C Relative permittivity 100 Hz - IEC 60250 3.5 10
C Relative permittivity 1 MHz - IEC 60250 3.2 3.7
C Dissipation factor 100 Hz 10-4 IEC 60250 60 1500
C Dissipation factor 1 MHz 10-4 IEC 60250 150 800
C Volume resistivity Ohm·m IEC 60093 1E11 1E10
C Surface resistivity Ohm IEC 60093 1E15 1E13
C Electric strength 1 mm kV/mm IEC 60243-1 43 43
C Comparative tracking index CTI Solution A V IEC 60112 600
Other properties (23 °C)
C Water absorption (Saturation value) Water at 23 °C % ISO 62 7.0
C Water absorption (Equilibrium value) 23 °C; 50 % RH % ISO 62 2.0
C Density kg/m³ ISO 1183 1180
Bulk density kg/m³ ISO 60 600
Processing conditions for test specimens
C Injection molding-Melt temperature °C ISO 294 280
C Injection molding-Mold temperature °C ISO 294 80
Processing recommendations
Drying temperature dry air dryer °C - 80
Drying time dry air dryer h - 2-6
Residual moisture content % Acc. to Karl Fischer 0.03-0.12
Melt temperature (Tmin - Tmax) °C - 260-290
Mold temperature °C - 80-100