PA6 BKV 30 XTS1 901510德国朗盛Durethan 30%玻纤高耐热老化稳定尼龙6塑料（18024445500）

PA 6, 30 % glass fibers, injection molding, heat-aging stabilized, notably high heat-aging stability



ISO Shortname: ISO1874-PA 6, GHR, 14-100, GF30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.25　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.63　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.14　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 9500 5300
C Nominal strain at break 50 mm/min % ISO 527-1,-2 3 5.5
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 170 85
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3 6
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 60　
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 10　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 9　
Izod impact strength 23 °C kJ/m² ISO 180-1U 50 70
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10 15
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 9　
Flexural modulus 2 mm/min MPa ISO 178-A 9400 5200
Flexural strength 2 mm/min MPa ISO 178-A 250 140
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3 5
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A　120