PA6 DP 2131/20 H2.0 900051德国朗盛Durethan 20%玻纤耐风化尼龙6塑料（18024445500）

PA 6, 20 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, improved resistance to weathering



ISO Shortname: ISO 1874 PA 6, GHR, 14-080, GF20

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.35　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.54　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.12　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.19　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 7600　
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 150　
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0　
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 45 60
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 40 40
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10　
Izod impact strength 23 °C kJ/m² ISO 180-1U 35　
Izod impact strength -30 °C kJ/m² ISO 180-1U 35　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 6400　
Flexural strength 2 mm/min MPa ISO 178-A 225　
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.5　
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 200　
C Puncture energy 23 °C J ISO 6603-2 5　
C Puncture energy -30 °C J ISO 6603-2 4