PA6 DP 2131/20 W1 901317德国朗盛Durethan 20%玻纤耐候表面光洁度改善尼龙6塑料(18024445500)
PA 6, 20 % glass fibers, injection molding, weather stabilized, improved surface finish
ISO Shortname: ISO 1874 PA 6, GHLR, 14-080, GF20
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 260 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.22
Molding shrinkage, transverse 150x105x3; 260 °C / MT 80 °C; 500 bar % acc. ISO 2577 0.67
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.07
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.20
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 7600 4700
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 150 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.0 7.0
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 45 60
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 40 40
C Charpy notched impact strength 23 °C kJ/m&sup2; ISO 179-1eA <10
C Charpy notched impact strength -30 °C kJ/m&sup2; ISO 179-1eA <10
Izod impact strength 23 °C kJ/m&sup2; ISO 180-1U 30 40
Izod impact strength -30 °C kJ/m&sup2; ISO 180-1U 30 30
Izod notched impact strength 23 °C kJ/m&sup2; ISO 180-1A < 10 < 10
Izod notched impact strength -30 °C kJ/m&sup2; ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 6400 4100
Flexural strength 2 mm/min MPa ISO 178-A 212 130
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.1 6.4
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 197 110
C Puncture energy 23 °C J ISO 6603-2 5 10
C Puncture energy -30 °C J ISO 6603-2 4
Ball indentation hardness N/mm&sup2; ISO 2039-1 198 |