PA6 BM 230 H2.0 901510德国朗盛Durethan 30%矿物耐热老化稳定尼龙6塑料（18024445500）

PA 6, injection molding, 30 % mineral, isotropic properties, heat-aging stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 6, MHR, 14-050, MD30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
Molding shrinkage, parallel 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 1.08　
Molding shrinkage, transverse 150x105x3; 280 °C / MT 80 °C; 500 bar % acc. ISO 2577 1.12　
Post- shrinkage, parallel 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.32　
Post- shrinkage, transverse 150x105x3; 120 °C; 4 h % acc. ISO 2577 0.3　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 5000 2000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 80 50
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 10 45
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 120 N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 80 80
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA < 10 13
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 122 N
Izod impact strength -30 °C kJ/m² ISO 180-1U 80 95
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Izod notched impact strength -40 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 4700 1800
Flexural strength 2 mm/min MPa ISO 178-A 140 60
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.5 8.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 130 55