PA6 BM 430 H2.0 901510德国朗盛Durethan 30%矿物热老化稳定尼龙6塑料（18024445500）

PA 6, 30 % mineral, injection molding, heat-aging stabilized



ISO Shortname: ISO 1874-PA 6, GHR, 14-040, MD30

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.2　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 1.1　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.3　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.2　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 4700 1450
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 70 35
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 5.0 >100
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 75 N
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 60 50
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA <10 <10
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA <10 <10
Izod impact strength 23 °C kJ/m² ISO 180-1U 65 N
Izod impact strength -30 °C kJ/m² ISO 180-1U 50 55
Izod notched impact strength 23 °C kJ/m² ISO 180-1A <10 <10
Izod notched impact strength -30 °C kJ/m² ISO 180-1A <10 <10
Flexural modulus 2 mm/min MPa ISO 178-A 4500 1590
Flexural strength 2 mm/min MPa ISO 178-A 120 48
Flexural strain at flexural strength 2 mm/min % ISO 178-A 5.0 7.8
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 115 35