PA6 BCF 30 X H2.0 901510µÂ¹úÀÊÊ¢Durethan 30%²£ÏË/̼ÏËÈÈÀÏ»¯Îȶ¨ÄáÁú6ËÜÁÏ£¨18024445500£©
PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improved electrical conductivity
ISO Shortname: ISO 1874-PA 6, GHR, 14-140, (GF+CF) 30
Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Melt volume-flow rate 260 ¡ãC; 5 kg cm³/(10 min) ISO 1133-1 15¡¡
Molding shrinkage, parallel 150x105x3; 280 ¡ãC / MT 80 ¡ãC; 500 bar % acc. ISO 2577 0.15¡¡
Molding shrinkage, transverse 150x105x3 % acc. ISO 2577 0.75¡¡
Post- shrinkage, parallel 150x105x3; 120 ¡ãC; 4 h % acc. ISO 2577 0.03¡¡
Post- shrinkage, transverse 150x105x3; 120 ¡ãC; 4 h % acc. ISO 2577 0.1¡¡
C Molding shrinkage, parallel 60x60x2; 280 ¡ãC / MT 80 ¡ãC; 600 bar % ISO 294-4 0.22¡¡
C Molding shrinkage, transverse 60x60x2; 280 ¡ãC / MT 80 ¡ãC; 600 bar % ISO 294-4 0.77¡¡
Post- shrinkage, parallel 60x60x2; 120 ¡ãC; 4 h % ISO 294-4 0.03¡¡
Post- shrinkage, transverse 60x60x2; 120 ¡ãC; 4 h % ISO 294-4 0.08¡¡
Mechanical properties (23 ¡ãC/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 13500 6700
C Nominal strain at break 50 mm/min % ISO 527-1,-2 3.5¡¡
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 185 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.9 5.0
C Charpy impact strength 23 ¡ãC kJ/m² ISO 179-1eU 75 80
C Charpy impact strength -30 ¡ãC kJ/m² ISO 179-1eU 60 60
C Charpy notched impact strength 23 ¡ãC kJ/m² ISO 179-1eA 11¡¡
C Charpy notched impact strength -30 ¡ãC kJ/m&sup2; ISO 179-1eA <10¡¡
Izod impact strength 23 ¡ãC kJ/m&sup2; ISO 180-1U 65 65
Izod impact strength -30 ¡ãC kJ/m&sup2; ISO 180-1U 60 60 |