PA66 RFL36L沙伯基础创新内部润滑低提取聚酰胺66尼龙塑料（18024445500）




Also known as:LNP™LUBRICOMP™Compound RFL-4036 LE


Product reorder name:RFL36L


　


LNP LUBRICOMP RFL36L is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.


　







Property

　




TYPICAL PROPERTIES (1)


MECHANICAL

Value

Unit

Standard




Tensile Stress, yield

1540

kgf/cm²

ASTM D 638




Tensile Stress, break

1540

kgf/cm²

ASTM D 638




Tensile Strain, yield

2.8

%

ASTM D 638




Tensile Strain, break

2.8

%

ASTM D 638




Tensile Modulus, 50 mm/min

105400

kgf/cm²

ASTM D 638




Flexural Stress

2170

kgf/cm²

ASTM D 790




Flexural Modulus

84300

kgf/cm²

ASTM D 790




Tensile Stress, yield

152

MPa

ISO 527




Tensile Stress, break

152

MPa

ISO 527




Tensile Strain, yield

2.8

%

ISO 527




Tensile Strain, break

2.8

%

ISO 527




Tensile Modulus, 1 mm/min

10050

MPa

ISO 527




Flexural Stress

230

MPa

ISO 178




Flexural Modulus

9300

MPa

ISO 178




IMPACT

Value

Unit

Standard




Izod Impact, unnotched, 23°C

102

cm-kgf/cm

ASTM D 4812




Izod Impact, notched, 23°C

9

cm-kgf/cm

ASTM D 256




Instrumented Impact Energy @ peak, 23°C

128

cm-kgf

ASTM D 3763




Multiaxial Impact

29

cm-kgf

ISO 6603




Izod Impact, unnotched 80*10*4 +23°C

61

kJ/m²

ISO 180/1U




Izod Impact, notched 80*10*4 +23°C

10

kJ/m²

ISO 180/1A




THERMAL

Value

Unit

Standard




HDT, 0.45 MPa, 3.2 mm, unannealed

261

°C

ASTM D 648




HDT, 1.82 MPa, 3.2mm, unannealed

252

°C

ASTM D 648




CTE, -40°C to 40°C, flow

7.38E-05

1/°C

ASTM E 831




CTE, -40°C to 40°C, xflow

2.88E-05

1/°C

ASTM E 831




CTE, -40°C to 40°C, flow

7.4E-05

1/°C

ISO 11359-2




CTE, -40°C to 40°C, xflow

2.9E-05

1/°C

ISO 11359-2




HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm

260

°C

ISO 75/Bf




HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

247

°C

ISO 75/Af




PHYSICAL

Value

Unit

Standard




Density

1.52

g/cm³

ASTM D 792




Moisture Absorption, 50% RH, 24 hrs

0.4

%

ASTM D 570




Mold Shrinkage, flow, 24 hrs (5)

0.4 - 0.6

%

ASTM D 955




Mold Shrinkage, xflow, 24 hrs (5)

1.3 - 1.5

%

ASTM D 955




Mold Shrinkage, flow, 24 hrs (5)

0.53

%

ISO 294




Mold Shrinkage, xflow, 24 hrs (5)

1.4

%

ISO 294




Wear Factor Washer

4

10^-10 in^5-min/ft-lb-hr

ASTM D 3702 Modified




Dynamic COF

0.66

-

ASTM D 3702 Modified




Static COF

0.65

-

ASTM D 3702 Modified




Density

1.52

g/cm³

ISO 1183






Source GMD, last updated:2008/09/24




Processing




Parameter


Injection Molding

Value

Unit


Drying Temperature

80

°C


Drying Time

4

hrs


Maximum Moisture Content

0.15 - 0.25

%


Melt Temperature

280 - 305

°C


Front - Zone 3 Temperature

295 - 305

°C


Middle - Zone 2 Temperature

280 - 295

°C


Rear - Zone 1 Temperature

265 - 275

°C


Mold Temperature

95 - 110

°C


Back Pressure

0.2 - 0.3

MPa


Screw Speed

30 - 60

rpm




Source GMD, last updated:2008/09/24




　


THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.





供应的沙伯基础PA66塑料如下：


LNP™ LUBRICOMP Compound




Grades

Description


RA004

Internally Lubricated Nylon 66 compound containing Aramid.



RAL22

Internally Lubricated Nylon 66 compound containing Aramid, PTFE.



RAL22I

Internally Lubricated, High Impact Nylon 66 compound containing PTFE, Aramid Fiber.



RAL22S

Internally Lubricated Nylon 66 compound containing PTFE, Aramid Fiber.



RAL23

Internally Lubricated Nylon 66 compound containing Aramid Fiber, PTFE.



RAL23S

Heat Stabilized Nylon 66 compound containing Aramid Fiber, PTFE.



RCL36S

Electrically Conductive Nylon 66 compound containing Carbon Fiber, PTFE.
:


RCP36

Electrically Conductive Nylon 66 compound containing Silicone, PTFE, Carbon Fiber.



RFL16

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.



RFL26S

Internally Lubricated, Heat Stabilized Nylon 66 compound containing Glass Fiber, PTFE.



RFL33

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.


RFL34

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE.


RFL36L

Internally Lubricated, Low Extractible Nylon 66 compound containing Glass Fiber, PTFE.


RFP36

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.


RFP36XXZ

PA 66, Silicone, Lubricants, PTFE, Glass, Internally Lubricated, Wear resistant,


RN001S

Internally Lubricated, Heat Stabilized Nylon 66 compound containing MOS2.


RP003

Internally Lubricated Nylon 66 compound containing PTFE, Silicone.


RP004

Internally Lubricated Nylon 66 compound containing PTFE, Silicone.


RX01514

Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).


RX03643H

Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).


RX05496

Internally Lubricated Nylon 66 compound containing Glass Fiber, PTFE, Silicone.


RX06480

Internally Lubricated Nylon 66 compound containing PTFE, Glass Fiber, Silicone.


RX85514

Internally Lubricated Nylon 66 compound containing Proprietary Filler(s).