PA66 AKV 325 H2.0 901510德国朗盛Durethan 25%玻纤挤出吹塑热老化稳定水解稳定尼龙66塑料（18024445500）

PA 66, 25 % glass fibers, extrusion, blow molding, heat-aging stabilized, hydrolysis stabilized

ISO/ ASTM

ISO Shortname: ISO 1874-PA 66, EH, 14-080, GF25

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.8　
C Molding shrinkage, transverse 60x60x2; 280 °C / MT 80 °C; 600 bar % ISO 294-4 0.8　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.1　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 8200 5000
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 150 100
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 3.8 10
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 80 90
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 65 65
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA < 10 15
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA < 10 < 10
Izod impact strength 23 °C kJ/m² ISO 180-1U 70 70
Izod impact strength -30 °C kJ/m² ISO 180-1U 60 55
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10 15
Izod notched impact strength -30 °C kJ/m² ISO 180-1A < 10 < 10
Flexural modulus 2 mm/min MPa ISO 178-A 7200 4200
Flexural strength 2 mm/min MPa ISO 178-A 240 140
Flexural strain at flexural strength 2 mm/min % ISO 178-A 4.7 7.0
Flexural stress at 3.5 % strain 2 mm/min MPa ISO 178-A 220 105