PA66 AKV 35 CX H2.0 900876德国朗盛Durethan 35%玻纤热老化稳定注塑尼龙66塑料（18024445500）

PA 66, 35 % glass fibers, injection molding, heat aging stabilized



ISO Shortname: ISO 1874-PA 66, GHR, 12-110, GF35

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.3　
C Molding shrinkage, transverse 60x60x2; 290 °C / MT 80 °C; 600 bar % ISO 294-4 0.9　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.07　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.07　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 11000　
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 197　
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.8　
Izod impact strength 23 °C kJ/m² ISO 180-1U 58　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 10　
Flexural modulus 2 mm/min MPa ISO 178-A 10900　
Flexural strength 2 mm/min MPa ISO 178-A 296　
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.2　

Thermal properties
C Melting temperature 10 °C/min °C ISO 11357-1,-3 260　
C Temperature of deflection under load 1.80 MPa °C ISO 75-1,-2 >240　

Other properties (23 °C)
C Density　kg/m³ ISO 1183 1413